How is toughening agent applied to PP modification

An adequate quantity of an antioxidant or anti-aging masterbatch is added to the plastic in order to provide it high weather resistance. Following testing, the test item is exposed to UV light from a xenon lamp for 1000 hours, or one year. The tensile strength and impact strength remain unaffected. 88% and 86%, respectively, are the rates. Impact strength and tensile strength retention rates are 74% and 71%, respectively, whereas the duration of Xenon lamp UV radiation is 3000h, or three years. Long service lives and little environmental contamination from waste plastics are both benefits of plastic's remarkable age resistance.

Applied toughener to PP modification

Один из пяти пластиков общего назначения, полипропилен имеет ограниченное применение в инженерных пластиках и конструкционных материалах из-за значительного снижения скорости формования, быстрого коробления и деформации. Систему укрепляют, корректируют и добавляют карбонат кальция. Композитный материал может достигать различных типичных механических качеств при меньшей стоимости, что расширяет спектр применения полипропилена.

1. Calcium carbonate activation

With the growing growth of the composite material sector, toughener producers have discovered that calcium carbonate serves as both a filler and a significant modifier. Calcium carbonate may be added to the polypropylene blending modification method to increase stiffness and heat resistance while lowering the product's cost of raw materials and molding shrinkage ratio.

Calcium carbonate, on the other hand, is an inorganic filler that is compatible with polypropylene. Since the capacity is low, activation treatment is needed before use to strengthen the bonds between the molecular chains of the polymer and the calcium carbonate and to enhance the mechanical qualities of filled polypropylene materials. The producers of tougheners advise employing hefty calcium carbonate with a mesh size of at least 1000. Activate the calcium carbonate by placing it in a high-speed agitator after drying, adding the required amount of phosphate ester coupling agent, and stirring at a high speed for 15 to 20 minutes. Alternatively, use active ground calcium carbonate with a mesh size of 1000 or higher.

The impact strength of the system in the blending system grows fast at initially, increases slowly after 30 parts, and falls after 40 parts as the amount of activated calcium carbonate increases. The coupling agent can increase the impact of the substance by activating the calcium carbonate. Because the activated calcium carbonate particle surface's physical and chemical characteristics have altered and are now simpler to distribute in the matrix, the strength has increased. There will be an aggregation and buildup of inorganic particles when the calcium carbonate content surpasses a particular threshold, making the blending method ineffective. The structure develops internal flaws, which cause a deterioration in a number of mechanical qualities. Consequently, the dosage of calcium carbonate should not exceed 40 parts.

PP(1)

2. How a toughening agent affects the mixing system

In order to give PP superior toughness and outstanding processability, tougheners are utilized.

(2) The chemical structure of the toughening agent, which has high aging resistance, has no unsaturated double bonds.

(3) Упрочняющий агент является текучим и совместимым с полиолефинами, а также имеет узкое молекулярно-массовое распределение.

(4) Прочность линии сварки и дисперсионное воздействие наполнителей могут быть улучшены за счет хорошей текучести.

The impact strength and elongation at break of the system are significantly increased with the addition of toughener. As can be shown, PP and activated calcium carbonate are compatible with the toughening agent, which also has a good toughening effect on PP. This is due to the narrow molecular weight distribution of the toughening agent and the longer side octyl group than the side ethyl group in the molecular structure, which can form a molecular connection point and function as a connection and buffer between the components, allowing the system to function when it is impacted.

As impact energy is distributed and buffered, there is less chance that stress-induced crazes will turn into fractures, increasing the system's impact resistance.

Сетевая структура, образованная этими местами соединения, может испытывать значительную деформацию при растяжении системы, что приводит к значительному увеличению удлинения системы' при разрыве. Поскольку характеристики упрочняющего агента сами по себе определяют прочность на растяжение, прочность на изгиб и модуль упругости системы, при увеличении содержания упрочняющего агента его содержание должно быть ниже 20%.

недавно статьи

Как выбрать подходящий малеиновый ангидрид, привитый POE, для повышения прочности нейлона?

Coace® W1A-F разработан специально для использования в качестве замедлителя ударных нагрузок для PA6, PA66 и полиамидных систем, нуждающихся в усилении и наполнении. Его особые качества делают его идеальным выбором для использования там, где наиболее важны повышенная ударопрочность и вязкость.

Читать далее →

Новый прорыв в модификации ПБТ: революционное применение упрочняющего агента POE-g-GMA

Использование упрочняющего агента POE-g-GMA в модификации ПБТ не только устраняет хрупкость ПБТ-материалов, но и дает новые направления развития пластиковой промышленности.

Читать далее →

При добавлении наполнителей в композиционные материалы PP/PE необходимо ли добавлять компатибилизатор?

Если вы хотите изучить возможности использования компатибилизаторов PP-g-MAH, свяжитесь с профессиональным поставщиком химикатов, который предоставит образцы и окажет техническую поддержку. Консультации с COACE помогут подобрать смеси, отвечающие определенным требованиям.

Читать далее →