Products Description
A complete solution for improving the adhesion qualities and compatibility of PA/PPE blends is provided by our specially developed anhydride PPE coupling agent and compatibilizer. It gives producers and suppliers the tools to optimize their PA/PPE blend formulations for a variety of markets and applications thanks to its superior adhesion capabilities, increased compatibility, adaptability, thermal stability, and improved mechanical properties. You can improve the adhesion, mechanical performance, and product reliability of your PA/PPE blend products by using our product. Unlock the full potential of your PA/PPE blend compositions by investing in our specially designed anhydride PPE right away.
Advanced Equipment!
Equipped with advanced production lines and experimental testing center to ensure product quality.
Advanced Equipment!
Equipped with advanced production lines and experimental testing center to ensure product quality.
Mechanical properties of PPO/PA66/GF systems without and with CS-1 added
| Formula | 1#（%） | 2#（%） |
| PPO | 30 | 25 |
| PA66 | 30 | 30 |
| SEBS | 7 | 7 |
| GF | 33 | 33 |
| CS-1 | 0 | 5 |
| Performance | Unit | 1# | 2# | |
| DensityMelt flow rate （MFR） | g/cm3 | 1.32 | 1.32 | |
| condition：280℃2.16kg | g/10min | 6.8 | 7.9 | |
| Heat distortion temperature（HDT） | 0.45MPa，120℃/h | ℃ | 236.9 | 237.2 |
| 1.82MPa，120℃/h | ℃ | 204.6 | 204.8 | |
| tensile strength | Mpa | 105.3 | 136.5 | |
| tensile rate | % | 1.3 | 3.6 | |
| Bending strength | Mpa | 142.6 | 191.6 | |
| Flexural modulus | Mpa | 6150 | 6270 | |
| Izod notched impact strength | J/m | 65 | 132 | |
| Izod unnotched impact strength | J/m | 216 | 597 | |
It can be seen from the above table that adding 5% CS-1, the tensile strength elongation at break, flexural strength and impact strength of the PPO/PA66/GF system are significantly improved, and the flexural modulus has little effect.
Application case two
Mechanical properties of PPO/PA66/GF systems without and with CS-1 added
| Formula | 1#（%） | 2#（%） |
| PPO | 45 | 40 |
| PA66 | 45 | 45 |
| SEBS | 10 | 10 |
| CS-1 | 0 | 5 |
| Performance | Unit | 1# | 2# | |
| densityMelt flow rate （MFR） | g/cm3 | 1.078 | 1.075 | |
| Condition : 280℃2.16kg | g/10min | 12.8 | 10.2 | |
| Heat distortion temperature （HDT） | 0.45MPa，120℃/h | ℃ | 192.6 | 188.5 |
| 1.82MPa，120℃/h | ℃ | 110.3 | 107.3 | |
| tensile strength | Mpa | 42.6 | 55.8 | |
| tensile rate | % | 3.1 | 76.5 | |
| Bending strength | Mpa | 58.3 | 59.6 | |
| Flexural modulus | Mpa | 1820 | 1790 | |
| Lzod notched impact strength | J/m | 28 | 268 | |
| Lzod unnotched impact strength | J/m | 253 | NB | |
It can be seen from the above table that the addition of 5% CS-1 increases the tensile strength, elongation at break and impact strength of the alloy system significantly, but has little effect on the flexural strength and flexural modulus.
Recommended dosage
3-8%, which can be increased or decreased in moderation according to the actual application, taking into account the cost.
Packaging and Storage
25KG kraft paper bag lined with plastic bag, as non-dangerous goods, avoid sunlight and rain.
Characteristic
CS-1are granules with yellow color, low odor. It can be used in PPO/PA66/GF33 System.
| Physical | Nominal values | Test method(s) |
| Density | 1.02g/cm³ | ASTM D792 |
| Melt flow rate(190℃、2.16kg） | 8-15g/10min | ASTM D1238 |
| Maleic anhydride content | Middle | Internal method |
| appearance | pellet |
Our advantage
Global Supply Chain!
Sound Storage And Logistics Supply Chain System
Technical Support
After-sales protection
Focus • Achievement • Excellence!
Products Customized
Focus on R&D
Global Services
Coace Certification!
ISO9001:2015 Certification
ISO14001:2015 Certification
EU REACH registration
Korea K-REACH pre-registration
Enterprise advantage!
Layout at home and abroad, wonderful for mixing
Domestic marketing layout
Overseas marketing layout
Application
It can be seen from Figure 1 that the PPO phase of the alloy system without compatibilizer is large in size and irregular in size, showing a typical dual-continuous phase structure. Add 5%CS-1, the size of the dispersed phase is obviously reduced, and it is a regular spherical shape with uniform distribution.
It can be used as compatibilizer of polyamide and polyphenylene oxide alloy.Solutions by industryThe following areas see considerable use of the specially formulated anhydride PPE coupling agent and compatibilizer:Automotive: This product is excellent for improving the performance of PA/PPE blends used in automotive applications, such as electrical connectors, under-the-hood components, and interior automobile components. By enhancing the adherence of PA and PPE, it ensures the dependability and durability of automotive parts in challenging conditions.
Electrical and electronic applications, such as connections, switches, and housings, require the PA/PPE mixes’ qualities to be optimized, which calls for the coupling agent. It improves the compatibility and adherence of the two polymers, resulting in good thermal stability and electrical insulation.
Industrial Equipment: Our specially formulated anhydride PPE is ideal for PA/PPE blends used in applications for industrial equipment, such as gears, bearings, and pump components. It enhances mechanical qualities and wear- and friction-resistance, ensuring dependable performance in industrial situations.
Consumer Goods: The qualities of PA/PPE blends used in the manufacture of consumer goods, such as toys, athletic equipment, and appliances, must be improved with the use of this coupling agent. It improves the adherence of PA and PPE, producing goods that are robust, impact-resistant, and aesthetically pleasing.