Maleic anhydride modified linear low density polyethylene polyolefin alloy compatibilizer low smoke halogen free flame retardant W1L

모형: W1L

소개:

W1L is a general-purpose LLDPE-g-MAH product with excellent comprehensive properties.
est item 테스트 데이터 테스트 방법
밀도 0.92g/cm³ ASTM D792
용융 유량(190°C/2.16kg) 0.5-2.0 g/10min ASTM D1238
말레산 무수물 함량 높음 콜본드 방법 1
수분 ≤0.3 % 할로겐 빠른 수분 측정
외관 세분화
제품 설명

저연 할로겐 프리 난연 케이블 소재의 기본 공식

공식 1#(%) 2#(%)
magnesium hydroxide/MH-8800 60 60
LLDPE/FL201XV/Exxon Mobil 20 15
EVA/7350M/Formosa Plastics 20 20
W1L 0 5

It can be seen from Figure 1 that the addition of 5% W1L increases the tensile strength of the low-smoke halogen-free flame retardant cable compound system by 90% and the elongation at break by 135%.

Improvement of tensile properties of low-smoke halogen-free flame retardant cable material

1

Application effect of W1L in talc (20%) filled LLDPE system

2-1

Effect of W1L on Tensile Properties of Talc (20%) Filled LLDPE System

3

It can be seen from the figure that in the LLDPE system filled with talc (20%), adding 3% W1L can greatly improve the tensile strength, flexural strength and notched impact strength of the material system.

권장 복용량:The dose (5-25%) may be increased or decreased properly according to the toughness requirements and by taking the cost into consideration.3-10% shall be adopted for PA6/PA66 reinforcing and toughening, while 5% shall be adopted for the compatibilizer of nylon and polypropylene/polyethylene alloy.

포장, 보관 및 운송:내부 비닐 봉투가 있는 20kg 크래프트 백. 본 제품은 위험물이 아닌 물품으로 취급하며 건조한 상태에서 보관 또는 운송해야 하며 햇빛과 비를 피해야 합니다.

특성

 

W1L is a method of chemical reaction to connect maleic anhydride molecules on the linear low-density polyethylene molecular chain, so that the polyethylene end has the re-reactivity and strong polarity of maleic anhydride polar molecules, so it can improve polyolefin. The interface affinity between the substrate and inorganic substances such as metal powder, glass fiber, wood powder, mineral powder, starch, etc., so as to enhance the strength of the composite material, and is often used as a compatibilizer for polyolefin materials. When this product is used in low-smoke halogen-free flame retardant cable compound, it can improve the compatibility and adhesion between polyolefin matrix and inorganic flame retardant interface. Improve the dispersibility and compatibility of magnesium hydroxide and aluminum hydroxide, so as to maximize the flame retardancy of cable materials, reduce smoke index, smoke generation, calorific value and carbon monoxide generation, increase oxygen index, improve dripping Falling properties, etc., improve the mechanical properties of materials. This product can also be used as a surface improver for extruded sheet or extruded sheet, which can effectively improve the surface flatness of sheet or sheet, and eliminate unevenness and pitting on the surface of the material.

 

고급 장비!

제품 품질을 보장하기 위해 첨단 생산 라인과 실험 테스트 센터를 갖추고 있습니다.

강력한 기술력!

10명 이상의 숙련된 기술 R&D 직원이 지속적인 혁신을 주도합니다.

 

이점

 

(1) High flame retardant efficiency, which can endow plastic materials with good flame retardancy;
(2) It has good compatibility with plastic resins and can be well dispersed in resins to form a homogeneous system;
(3) Does not decompose at the processing temperature of the plastic;
(4) Do not reduce the mechanical properties, electrical properties, weather resistance, etc. of plastics;
(5) It has good durability and can be kept in plastic for a long time to play a flame-retardant role;
(6) Non-toxic, odorless, and pollution-free, no toxic gas is produced during the flame-retardant process, and no secondary pollution occurs.

 

당사의 장점

글로벌 공급망!

사운드 스토리지 및 물류 공급망 시스템
기술 지원
판매 후 보호

집중 - 성취 - 우수성!

맞춤형 제품
R&D에 집중
글로벌 서비스

코이스 인증!

ISO9001:2015 인증
ISO14001:2015 인증
EU REACH 등록

한국 K-REACH 사전 등록

기업의 이점!

국내외를 넘나드는 레이아웃, 믹스 앤 매치하기 좋은 디자인
국내 마케팅 레이아웃
해외 마케팅 레이아웃

 

애플리케이션

11. it Can be used as a compatibilizer for low-smoke halogen-free flame retardant cable materials;
2. 압출 시트 / 플레이트의 표면 개선제로 사용할 수있어 재료의 표면 평탄도를 효과적으로 개선하고 재료 표면의 요철과 피팅을 제거 할 수 있습니다;
3. 폴리에틸렌과 유리 섬유의 호환성을 촉진하기 위해 폴리에틸렌과 유리 섬유의 호환제로 사용할 수 있습니다;
4. 컬러 마스터 배치, 난연성 마스터 배치, 기능성 마스터 배치 등과 같이 PE를 캐리어로 사용하는 마스터 배치의 호환제로 사용할 수 있습니다;
5. 김서림 방지 멀치의 김서림 방지 기간을 연장하기 위한 수식어로 사용할 수 있습니다.

 

 

문의 양식

좋아할지도 모릅니다.

배리어 필름 포장재 호환기

모형: W1L

소개:

COACE의 W1L은 비극성 사슬에 극성을 도입하는 MAH를 접목한 폴리에틸렌 기반 소재입니다.


배리어 필름 포장용 재료 호환제는 적응성과 효과를 모두 갖춘 첨가제로, 배리어 필름 포장에 사용되는 재료의 호환성, 배리어 성능 및 기계적 강도를 향상시킵니다.

 

자세히 보기 →

태양광 접착 필름용 글리시딜 메타크릴레이트 접목 안티-PID 첨가제

모델 번호: R2320

소개:

R2320은 에폭시 그룹이 기능화된 EVA 안티-PID 첨가제입니다.


자세히 보기 →

분해 가능한 폴리에스테르 소재 체인 익스텐더 핵 생성제

모델 번호: BP-5

소개:

Coace® BP-5 체인 익스텐더는 분해 가능한 폴리에스테르 체인을 효과적으로 연장 및 핵 형성하고 냉각 및 성형 속도를 높이며 점도를 높이고 필름과 시트의 인장 강도 및 펑크 저항성을 개선합니다.


자세히 보기 →

Ultra-High Fluidity Maleic Anhydride Modified Polypropylene Compatibilizer

모형: B1F

소개:

The polypropylene compatibilizer known as Coace ® B1F is modified with maleic anhydride, and it possesses a high grafting rate and a very high fluidity.


자세히 보기 →

메시지 남기기