Descrizione dei prodotti
W1A is prepared by grafting maleic anhydride by POE reaction. Since it introduces a strongly polar side group (maleic anhydride) on the main chain of POE molecule, maleic anhydride grafted POE can become a polar material. A bridge for adhesion and compatibility with non-polar materials. In the application of nylon + glass fiber modification, it can react with the glass fiber after surface treatment to improve the compatibility of nylon and glass fiber, thereby improving the tensile strength and impact strength of nylon. W1A can be used as both a compatibilizer and a toughening agent. As a nylon compatibilizer, it is also suitable for PA/PE and PA/PP alloys, which can improve the toughness of the alloy. As a nylon toughening agent, its low temperature The performance is very superior, the impact strength of PA6+15%W1A at -40ºC can be maintained at 35-40% of the impact at room temperature.
A bridge for adhesion and compatibility with non-polar materials. In the application of nylon + glass fiber modification, it can react with the glass fiber after surface treatment to improve the compatibility of nylon and glass fiber, thereby improving the tensile strength and impact strength of nylon. W1A can be used as both a compatibilizer and a toughening agent. As a nylon compatibilizer, it is also suitable for PA/PE and PA/PP alloys, which can improve the toughness of the alloy. As a nylon toughening agent, its low temperature The performance is very superior, the impact strength of PA6+15%W1A at -40℃ can be maintained at 35-40% of the impact at room temperature.
Typical application:
1. Rinforzo in nylon per la tempra
2. Riempimento in nylon composito
3. Nylon, polipropilene, polietilene miscelati con compatibilizzante aureo
| Prodotto | Aspetto | Indice di fusione (190ºC,2.16kg):g/10min |
Rapporto di innesto | Density(g/) |
| W1A |
White or light yellow even granules | 0.5-1.5 | alto | 0.87 |
| Features: This produce is ethylene elastomer with functionalized maleic anhydride,which is especially suitable for super-tough or cold-resistant nylon. | ||||
| Application:
1.Be used for PA6 or PA66 compatibilizing or toughening. Increase the impact resistance and processability of nylon,decrease the water absorption,greatly improve the cold-resistance. |
||||
Reaction principle
Il POE è un elastomero copolimero casuale di etilene e α-olefine ad alto contenuto di carbonio (1-butene, 1-esene, 1-ottene, ecc.) catalizzato da catalizzatori metallocenici. Presenta eccellenti proprietà meccaniche, reologiche e di resistenza ai raggi UV. Inoltre, il POE presenta anche i vantaggi di una buona affinità con le poliolefine e di una buona tenacità alle basse temperature, ed è ampiamente utilizzato per la tempra e la modifica di polimeri non polari come il polipropilene (PP) e il polietilene (PE).
Il POE è un elastomero non polare con scarsa compatibilità con i materiali polari, che non favorisce la modifica e il rinforzo di polimeri polari come la poliammide (PA) e il polietilene tereftalato (PET). La pratica comune consiste nell'eseguire prima la modifica dell'innesto sul POE e nell'innesto di composti a basso peso molecolare contenenti gruppi funzionali polari sulle macromolecole, cambiando così la polarità della catena molecolare del POE e migliorando la sua compatibilità con i polimeri polari. In questo modo può essere applicato alla modifica dei polimeri polari. I monomeri d'innesto comunemente utilizzati per il POE sono l'anidride maleica (MAH), il glicidilmetacrilato (GMA), l'acido metacrilico (MAA), l'acido acrilico (AA) e simili.
Il POE-g-MAH (anidride maleica innestata nel POE) si ottiene innestando il monomero altamente reattivo anidride maleica (MAH) mediante estrusione reattiva con l'elastomero POE come matrice. Il POE-g-MAH può essere utilizzato come buon agente indurente e compatibilizzante. Il suo effetto tenacizzante è migliore di quello del POE puro senza innesto. È adatto per PA, PP, PE, PC, ABS, PET, PBT, ecc. Compatibilità e tenacità dei materiali in lega.
Company Profile
Coace Chemical Company Limited is located in Xiamen Special Economic Zone, China. It is a national high-tech enterprise integrating R&D, production and sales of polymer materials, specializing in R&D, production, sales and service of plastic compatibilizers and toughening agents.
For more than ten years, the company has been adhering to the business philosophy of “stable quality, refinement and globalization”, serving the market, the factory owns 50,000 square-meter area and nearly 100 employees, including 20 technical R&D personnel, and is equipped with eight modern extruding-pellets systems production lines, which ensure the annual capacity of ten thousand metric tons. The products cover compatibilizers, coupling agents, impact modifiers, and other functional additives. and obtained ISO9001 quality management certification, with an annual production capacity of 20,000 tons.
Attrezzature avanzate!
Dotata di linee di produzione avanzate e di un centro di prove sperimentali per garantire la qualità del prodotto.
Forte forza tecnica!
Più di 10 esperti tecnici di R&S guidano l'innovazione continua.
Caratteristica
| Modelli di prodotto | W1A | W1A-2 |
| Indice di fusione |
0.3-1.0 |
0.3-1.0 |
| Tasso di innesto | Alto | Alto |
| densità | 0,87g/cm³ | 0,87g/cm³ |
| prestazioni | Riempimento rinforzato con PA, tempra a bassissima temperatura | Riempimento rinforzato con PA, tempra a bassissima temperatura |
| Typical application（advantages） | Application:
1.Be used for PA6 or PA66 compatibilizing or toughening. Increase the impact resistance and processability of nylon,decrease the water absorption,greatly improve the cold-resistance.2.Be used for the compatibilizer of nylon and polypropylene/polyethylene alloy.3.Be used for the macromolecular modifier(couling agent)of mineral-filled or grass-flber-filled nylon. |
Application:
1.Be used for PA6 or PA66 compatibilizing or toughening. Increase the impact resistance and processability of nylon,decrease the water absorption,greatly improve the cold-resistance.2.Be used for the compatibilizer of nylon and polypropylene/polyethylene alloy.3.Be used for the macromolecular modifier(couling agent)of mineral-filled or grass-flber-filled nylon. |
Il nostro vantaggio
Catena di approvvigionamento globale!
Sistema di stoccaggio e logistica della catena di approvvigionamento
Assistenza tecnica
Protezione post-vendita
Concentrazione - Risultati - Eccellenza!
Prodotti personalizzati
Focus su R&S
Servizi globali
Certificazione Coace!
Certificazione ISO9001:2015
Certificazione ISO14001:2015
Registrazione REACH UE
Corea K-REACH pre-registrazione
Vantaggio per le imprese!
Impaginazione in patria e all'estero, meravigliosa per la miscelazione
Layout di marketing nazionale
Layout di marketing all'estero
Applicazione
| Prestazioni | Unità | PA66 | PA6+30%GF+6%W1A |
| Resistenza alla trazione | MPa | 75 | 150 |
| Resistenza alla flessione | MPa | 102 | 215 |
| Lzod notched impact strength（23℃） | J/m | 80 | 200 |
Note：The above data are typical experimental values, for reference only, the viscosity of PA6 used in Table 3 is 2.8, and the viscosity of PA66 used in Table 4 is 2.7
Note:The data above are all experimental typical values, only for reference .
Suggested dose: The dose (5-25%) may be increased or decreased properly according to the toughness requirements and by taking the cost into consideration.3-10% shall be adopted for PA6/PA66 reinforcing and toughening, while 5% shall be adopted for the compatibilizer of nylon and polypropylene/polyethylene alloy.
Packaging, storage and transportation: 20kg kraft bag with internal plastic bag. This product shall be treated as non-hazardous article and be stored or transported under dry conditions, and sunlight and rain shall be avoided.