Introduzione:

W1L is a general-purpose LLDPE-g-MAH product with excellent comprehensive properties. The terminal has the reactivity and strong polarity of maleic anhydride polar molecules.
Articoli del test Dati del test Metodo di rilevamento
densità 0,95 g/cm³ ASTM D792  ISO 1183
punto di fusione 130℃266℉ ASTM D3418  ISO 3146
Dito fuso 1-3190℃2.16kgg/10min ASTM D1238  ISO 1133
Tasso di innesto High titolazione acido-base
Esterno particelle
Descrizione dei prodotti

 

In the cable production sector, PE-g-MAH, a low smoke, halogen-free flame retardant cable material compatibilizer, provides outstanding value and performance. This compatibilizer makes cable installations safer, more dependable, and compliant with regulations thanks to its increased flame retardancy, environmental friendliness, better cable performance, and broad application range. They can produce flame-resistant cables with lower smoke emissions and better mechanical qualities by integrating this cutting-edge product into their cable manufacturing processes. This will enable them to meet the exacting standards of a variety of industries, including building and construction, automotive, telecommunications, and industrial equipment.

W1L is a general-purpose LLDPE-g-MAH product with excellent comprehensive properties. The terminal has the reactivity and strong polarity of maleic anhydride polar molecules. It can improve the interface affinity between polyolefin base material and inorganic substances such as mineral powder, inorganic flame retardant, wood powder, starch, etc. It can enhance the strength of composite materials, and is widely used in low-smoke halogen-free flame retardant cable materials. The terminal has the reactivity and strong polarity of maleic anhydride polar molecules. It can improve the interface affinity between polyolefin base material and inorganic substances such as mineral powder, inorganic flame retardant, wood powder, starch, etc. It can enhance the strength of composite materials, and is widely used in low-smoke halogen-free flame retardant cable materials.

 

Attrezzature avanzate!

Dotata di linee di produzione avanzate e di un centro di prove sperimentali per garantire la qualità del prodotto.

Forte forza tecnica!

Più di 10 esperti tecnici di R&S guidano l'innovazione continua.

 

Caratteristica

 

The following data are derived from the average value of product retention sample testing within six months, and this data is updated every six months. The standard of grafting rate is: low <0.4%; medium 0.4%-0.8%; high ≥0.8%

 

Articoli del test Dati del test Metodo di rilevamento
densità 0,95 g/cm³ ASTM D792  ISO 1183
punto di fusione 130℃266℉ ASTM D3418  ISO 3146
Dito fuso 1-3190℃2.16kgg/10min ASTM D1238  ISO 1133
Tasso di innesto High titolazione acido-base
Esterno particelle

 

Dose consigliata:

3-10%, può essere aumentata o diminuita opportunamente in base ai requisiti di tenacità e tenendo conto dei costi.

Imballaggio, stoccaggio e trasporto:

Sacco kraft da 20 kg con sacchetto di plastica interno. Questo prodotto deve essere trattato come articolo non pericoloso e deve essere immagazzinato o trasportato in condizioni di asciutto, evitando la luce del sole e la pioggia.

 

Vantaggio

 

  • Enhanced Flame Retardancy: The flame retardancy of cable materials is greatly increased by the low smoke, halogen-free flame retardant cable material compatibilizer. It improves the safety of cable installations in residential, commercial, and industrial settings by successfully reducing the spread of flames, the production of smoke, and the emission of poisonous gasses.
  • Environmental friendliness: The use of flame retardants containing halogens, which are known to be harmful to the environment, is eliminated by PE-g-MAH. Through the compatibilizer’s halogen-free alternative, a safer and more environmentally friendly cable manufacturing process is ensured, as well as sustainability and compliance with strict environmental laws.
  • Better Cable Performance: By reinforcing the polymer matrix, the compatibilizer enhances the mechanical characteristics of cables, making them more resilient to impact, deformation, and mechanical stress. This benefit results in dependable cable performance, less maintenance needs, and longer service life.
  • Broad Application Range: Power, communication, and data cables are just a few of the cable types that PE-g-MAH is appropriate for. It offers flame retardancy and improved performance for a variety of applications, including industrial equipment, telecommunications, building wiring, and automobile wiring harnesses.

Il nostro vantaggio

Catena di approvvigionamento globale!

Sistema di stoccaggio e logistica della catena di approvvigionamento
Assistenza tecnica
Protezione post-vendita

Concentrazione - Risultati - Eccellenza!

Prodotti personalizzati
Focus su R&S
Servizi globali

Certificazione Coace!

Certificazione ISO9001:2015
Certificazione ISO14001:2015
Registrazione REACH UE

Corea K-REACH pre-registrazione

Vantaggio per le imprese!

Impaginazione in patria e all'estero, meravigliosa per la miscelazione
Layout di marketing nazionale
Layout di marketing all'estero

 

Applicazione
1. Materiale del cavo ritardante di fiamma senza alogeni a bassa emissione di fumo

2. Adhesive resin

use

Modifier for engineering plastics Adhesives for polar substrate Compounds compatibilizer

Proprietà tipiche

Fisico Valori nominali Metodo/i di prova
Densità 0.92g/cm³ ASTM D792   ISO 1183
Punto di fusione (DSC) 105(221°F) ASTM D3418   ISO 3146
Melt Flow Rate(190/2.16kg) 1-4 ASTM D1238   ISO 1133
Contenuto di anidride maleica medium Internal method
Aspetto pellet

 

 

Basic formula of low smoke halogen free flame retardant cable material

 

formula

1#(%)

2#(%)

idrossido di magnesio/MH-8800

60

60

LLDPE/FL201XV/Exxon Mobil

20

15

EVA/7350M/Formosa Plastics

20

20

W1L

0

5

 

It can be seen from Figure 1 that the addition of 5% COACE®W1L increases the tensile strength of the low-smoke halogen-free flame retardant cable compound system by 90% and the elongation at break by 135%.

 Improvement of tensile properties of low-smoke halogen-free flame retardant cable material

 

 

Modulo di richiesta

Potrebbe piacerti

Estensore di catena reattivo multifunzionale per materiali poliestere degradabili

Modello n.: BP-5

Introduzione:

Coace ® BP-5 è un estensore di catena reattivo multifunzionale in polvere.


Per saperne di più →

Modificatori d'impatto per PA6, PA66 con trattamento speciale

Modello n.: W1D

Introduzione:

W1D è un copolimero poliolefinico di anidride maleica utilizzato come modificatore d'impatto con un trattamento speciale.


Per saperne di più →

Additivi per film fotovoltaici funzionali al silano ad alta velocità di trasferimento

Modello n.: R2120

Introduzione:

Gli additivi per film R2120 presentano un'eccellente compatibilità con diversi materiali per film fotovoltaici, ottimizzando il tasso di trasferimento della luce incidente.


Per saperne di più →

Additivi silanici per film POE fotovoltaico

Modello n.: R1020

Introduzione:

Gli additivi silanici per film PV POE sono ingredienti speciali realizzati per migliorare le caratteristiche e l'efficienza dei film di incapsulamento in poliolefine, utilizzati nei moduli solari.


Per saperne di più →

LASCIATECI UN MESSAGGIO