coupling agent/compatibilizers used to strengthen the adhesion between PA and PP/ infill materials and polymer matrix.

Model No.: B1-1

Introduction :

Coace® B1-1 is a maleic anhydride modified polypropylene with high grafting rate.
 
Caractéristiques Valeur Unité Méthode d'essai

Apparence

Granulés
Couleur White translucent
Densité 0.92 g/cm3 ASTM D792
Débit de fusion(190℃2.16kg) 5-10 g/10min ASTM D1238
Teneur en anhydride maléique Haut wt% Méthode COACE[1]

Notes[1] LOW<0.4wt%; Middle(0.4wt%-0.8wt%); High≥0.8wt%.

Description des produits

 

Coace® B1-1 is a maleic anhydride modified polypropylene with high grafting rate.

When it comes to improving the adhesion between infill materials and the polypropylene matrix, coupling agents can be added to the polypropylene base compounds. Some commonly used coupling agents in polypropylene base compounds include:

1.Maleic Anhydride (MAH) Grafted Polymers: These are polymers that have been modified with maleic anhydride to introduce reactive groups that can bond with polar materials such as polyamides. They are used as compatibilizers to improve the adhesion between polyamide and polypropylene blends.

2.Isocyanate-based Coupling Agents: These are coupling agents that contain isocyanate groups which react with functional groups present on the surface of polyamides, such as amino and hydroxyl groups. They are used to improve the adhesion between infill materials and the polymer matrix.

3.Silane-based Coupling Agents: These are coupling agents that contain silane groups which bond with both organic and inorganic surfaces. They are used to improve the adhesion between glass fiber and the polymer matrix in composite materials, which can include blends of polyamides and polypropylene.

Overall, the use of coupling agents or compatibilizers is an effective approach to enhance the adhesion between PA and PP, as well as infill materials and polymer matrix. This can result in improved mechanical and thermal properties of the composite material.

When the grafting rate of the maleic anhydride onto the polypropylene is high, it means that a significant amount of maleic anhydride has been incorporated into the polymer backbone. This results in a copolymer with a higher density of reactive groups available to bond with polar materials, which can improve the adhesion between the polypropylene and other materials in a composite.

The high grafting rate of maleic anhydride onto polypropylene can also result in improved mechanical properties of the copolymer. The addition of maleic anhydride can increase the stiffness and strength of the material, while also improving its thermal stability.

Our coupling agents/compatibilizers are specialized additives made to improve the bonding of polyamide (PA) and polypropylene (PP) materials, as well as between infill materials and the polymer matrix. These goods are essential for enhancing the general effectiveness and longevity of diverse polymer-based applications. Our coupling agents/compatibilizers offer several benefits and find broad applications in sectors like automotive, construction, packaging, and more thanks to their remarkable compatibility and distinctive chemical makeup.

 

Un équipement de pointe !

Elle est équipée de lignes de production avancées et d'un centre d'essais expérimentaux pour garantir la qualité des produits.

Une force technique puissante !

Plus de 10 techniciens expérimentés en recherche et développement sont à l'origine d'une innovation permanente.

 

Caractéristique

 

Caractéristiques Valeur Unité Méthode d'essai

Apparence

Granulés
Couleur White translucent
Densité 0.92 g/cm3 ASTM D792
Débit de fusion(190℃2.16kg) 5-10 g/10min ASTM D1238
Teneur en anhydride maléique Haut wt% Méthode COACE[1]

Notes[1] LOW<0.4wt%; Middle(0.4wt%-0.8wt%); High≥0.8wt%.

 

Avantage
  • Improved Adhesion: Our coupling agents/compatibilizers greatly increase the adhesion of PA and PP materials, strengthening the connection and enhancing the mechanical characteristics of the composite material. Increased tensile strength, impact resistance, and general durability are all a result of this improved adhesion.
  • Greater Compatibility: Our coupling agents/compatibilizers’ special chemical make-up guarantees exceptional compatibility with both PA and PP materials as well as a range of infill materials. Because of this compatibility, the additives may be distributed and dispersed more evenly throughout the polymer matrix, which enhances homogeneity and performance overall.
  • Enhanced Thermal Stability: Due to their outstanding thermal stability, our coupling agents and compatibilizers can resist high processing temperatures without degrading. This quality is particularly significant in situations where the composite material is heated during production or usage.
  • Improved Impact Resistance: Our coupling agents/compatibilizers increase the impact resistance of the composite material by fortifying the bond between PA and PP components. In applications where impact resistance is crucial, such as automobile components or packing materials, this benefit is especially beneficial.
  • Versatile Uses: Our coupling agents and compatibilizers have a wide range of uses in a number of different sectors, including the automotive, building, packaging, and more. They may be used to improve the performance and longevity of a variety of polymer-based goods, including automotive components, pipelines, films, and packaging materials.

Notre avantage

service complet !

Selection recommendation
Support technique
Protection après-vente

service complet !

Selection recommendation
Support technique
Protection après-vente

service complet !

Selection recommendation
Support technique
Protection après-vente

service complet !

Selection recommendation
Support technique
Protection après-vente

 

Application
  • A utiliser comme agent de couplage dans les composés à base de polypropylène pour renforcer l'adhérence entre les matériaux de remplissage et la matrice polymère.
  • A utiliser comme compatibilisant pour améliorer la compatibilité entre le polyamide et le polypropylène.

 

 

Formulaire de demande de renseignements

Vous aimerez peut-être

Agent de couplage LLDPE modifié par anhydride pour les composés de câbles LSZH

Numéro de modèle : W1L-B

Introduction :

Coace ® W1L-B est un LLDPE modifié par un anhydride utilisé comme agent de couplage pour les composés à base de polyéthylène avec un taux de greffage élevé et une grande fluidité.


Lire la suite →

Mélange-maître inorganique anti-acidification pour film photovoltaïque EVA

Numéro de modèle : RM210A

Introduction :

RM210A est un mélange maître fonctionnel spécial à base de copolymère éthylène-acétate de vinyle.


Lire la suite →

Additif fonctionnalisé au silane pour les films photovoltaïques EPE

Numéro de modèle : R1120

Introduction :

L'additif pour film photovoltaïque Coace® R1120 présente les caractéristiques suivantes : haute résistivité volumique, haute transparence, faible point de cristallisation, etc.


Lire la suite →

Additifs pour films POE modifiés par des silanes

Numéro de modèle : R1030

Introduction :

Grâce à ses caractéristiques uniques, telles que la modification des silanes, une meilleure résistance aux UV, des capacités de barrière contre l'humidité et une stabilité de la température, il offre des avantages considérables en termes de longévité, de performances et de sécurité accrues.


Lire la suite →

LAISSEZ-NOUS UN MESSAGE