Nylonmodifikator mit hohem Elastizitätsmodul von Kautschuk und ultra-niedrigtemperaturgehärtetem PA

Modell-Nr.: W1P

Einführung:

Bei diesem Produkt handelt es sich um Ethylen-Propylen-Dien-Monomer mit funktionalisiertem Maleinsäureanhydrid, das sich besonders für superzähes oder kältebeständiges Nylon eignet.
Prüfling Testdaten Prüfverfahren
Dichte 0,87 g/cm³ ASTM D792

ISO 1183

Schmelzindex 0.1-0.4(190℃,2.16kg)g/10min ASTM D1238 ISO 1133
Veredelung Hoch Raten-Säure-Basen-Titration
Produkte Beschreibung

 

Our Nylon Modifier combines the advantages of nylon and rubber to improve the performance of many applications. It has a high elastic modulus of rubber and is toughened at extremely low temperatures. This special modifier is a great option for sectors needing durable and adaptable materials since it provides remarkable elasticity, high tensile strength, and increased low-temperature toughness.The nylon modifier is intended to improve the characteristics of polyamide (PA) materials, such as nylon, by combining high rubber elastic modulus with ultra-low temperature toughened PA. This modifier dramatically raises the composite’s elasticity and hardness by adding rubber particles to the PA matrix. Rubber’s high elastic modulus guarantees outstanding flexibility and resilience, and its ability to toughen at extremely low temperatures enables it to resist extremely cold temperatures without losing its mechanical integrity.

W1P is ethylene-propylen-diene monomer with functionalized maleic anhydride,which is especially suitable for super-tough or cold-resistant nylon.

It is functionalized with maleic anhydride, which is a chemical compound commonly used in the production of plastics and resins. This modification enhances the compatibility of the W1P with other materials, particularly nylon, and improves its overall toughness and resistance to cold temperatures.

Super-tough or cold-resistant nylon is a specific type of nylon that is designed to withstand harsh environmental conditions, such as extreme cold or impact forces. W1P is particularly well-suited for use in these types of applications because of its unique properties and compatibility with nylon. It can be used in a variety of products, including automotive parts, electrical components, and industrial equipment, among others.

 

Fortschrittliche Ausrüstung!

Ausgestattet mit fortschrittlichen Produktionslinien und einem experimentellen Testzentrum zur Gewährleistung der Produktqualität.

Starke technische Kraft!

Mehr als 10 erfahrene technische F&E-Mitarbeiter sorgen für kontinuierliche Innovation.

 

Charakteristisch

 

Prüfling Testdaten Prüfverfahren
Dichte 0,87 g/cm³ ASTM D792

ISO 1183

Schmelzindex 0.1-0.4(190℃,2.16kg)g/10min ASTM D1238 ISO 1133
Veredelung Hoch Raten-Säure-Basen-Titration

Table1:Typical Data of Toughening of PA6 Resin

PA6PA6+15%W1PPA6+20%W1P

Leistung Einheit PA6 PA6+15%W1P PA6+20%W1P
Zugfestigkeit MPa 60 55 50
Biegefestigkeit MPa 90 80 70
Lzod Kerbschlagzähigkeit (23℃)J/m 80 700 1000

Table2:Typical Data of Toughening of PA66 Resin

Leistung Einheit PA66 PA66+15%W1P PA66+20%W1P
Zugfestigkeit MPa 75 57 55
Biegefestigkeit MPa 102 85 80
Lzod Kerbschlagzähigkeit (23℃)J/m 80 800 1000

Vorteil

 

  • Increased Elasticity: By adding rubber particles to the PA matrix, the material gains extraordinary elasticity that allows it to tolerate repeated stretching and bending without permanently deforming. This qualifies it for uses like automobile parts, sporting goods, and industrial machinery parts, which call for flexibility and resilience.
  • exceptional Tensile Strength: The Nylon Modifier demonstrates exceptional tensile strength, assuring the durability and dependability of the finished product. It combines a high elastic modulus of rubber with an ultra-low temperature toughened PA. This qualifies it for high mechanical performance load-bearing applications such structural parts, gears, and bearings.
  • Increased Low-Temperature Toughness: This modifier’s capacity to toughen at extremely low temperatures enables the material to keep its mechanical qualities even in very cold settings. This makes it perfect for use in fields where exposure to low temperatures is widespread, including aerospace, automotive, and outdoor equipment.
  • Versatility: The Nylon Modifier with High Elastic Modulus of Rubber and Ultra-Low Temperature Toughened PA is a flexible solution for numerous industries and is simple to include into current PA formulations. To meet certain performance demands, it can be used either alone or in a blend with additional additives.

Unser Vorteil

Globale Lieferkette!

Solide Lagerung und Logistik Supply Chain System
Technische Unterstützung
Schutz nach dem Verkauf

Fokus - Leistung - Exzellenz!

Maßgeschneiderte Produkte
Fokus auf F&E
Globale Dienstleistungen

Coace-Zertifizierung!

ISO9001:2015 Zertifizierung
ISO14001:2015 Zertifizierung
EU REACH-Registrierung

Korea K-REACH Vorregistrierung

Vorteil für Unternehmen!

Layout im In- und Ausland, wunderbar zum Mischen
Gestaltung der Inlandsvermarktung
Layout für die Vermarktung in Übersee

 

Anmeldung

 

  • W1P kann für PA6 PA66 oder PP superzäh verwendet werden. Es erhöht die Kälteschlagzähigkeit und die Verarbeitbarkeit des Materials, verringert die Wasseraufnahme und verbessert die Kältebeständigkeit erheblich.
  • Es kann für die Kompatibilisierung von Nylon und Polypropylen-Legierungen verwendet werden.

 

 

 

 

Anfrage-Formular

Das könnte Ihnen gefallen

Mit Glycidylmethacrylat gepfropftes Anti-PID-Additiv für photovoltaische Klebefolien

Modell Nr.: R2320

Einführung:

R2320 ist ein mit Epoxidgruppen funktionalisiertes EVA-Anti-PID-Additiv.


Mehr lesen →

Schlagzähmodifikatoren für flammhemmende Polyamid-Compounds

Modell-Nr.: W1A-4

Einführung:

Coace ® W1A-4 is an anhydride modified polyolefin elastomer as impact modifiers with high graftingrate, which has low glass transition temperature.


Mehr lesen →

Mehrschichtige co-extrudierte Verpackungsfolie Kompatibilisator

Modell-Nr.: W1L

Einführung:

Bei W1L von COACE handelt es sich um Polyethylen als Basismaterial, das mit MAH gepfropft ist, wobei polare Seitengruppen in die unpolare Kette eingeführt werden. Es ist ein Klebstoff für polare und unpolare Materialien.

Mehr lesen →

Ultra-High Fluidity Maleic Anhydride Modified Polypropylene Compatibilizer

Modell-Nr.: B1F

Einführung:

The polypropylene compatibilizer known as Coace ® B1F is modified with maleic anhydride, and it possesses a high grafting rate and a very high fluidity.


Mehr lesen →

HINTERLASSEN SIE UNS EINE NACHRICHT