Preparation of maleic anhydride grafted polypropylene composite film

Nylon film has the advantages of light weight and easy processing, making it the preferred barrier material, but its application is limited by its poor gas barrier properties.

Graphene is a material with a two-dimensional mesh structure and has excellent gas barrier properties.

In this paper, modified graphene oxide (mGO-ODA) was produced by reducing graphene oxide (GO) with octadecylamine (ODA) and compounded with polypropylene maleic anhydride graft (MAPP) to prepare a series of mGO-ODA/MAPP composites as coatings.

Later, the coating materials were laminated onto the nylon film by spraying technique to obtain a nylon composite film with excellent gas barrier properties.

72c735c7f3255803e0e79c034f79b64

Figure (1) SEM images of tensile sections of (a) pure MAPP; (b) 15% mGO-ODA/MAPP; (c) 30% mGO-ODA/MAPP, (d) 45% mGO-ODA/MAPP; (e) 60% mGO-ODA/MAPP

ebc64c9f9c57c36dd4395f83ea83eb7

Figure (2) SEM images of cross-sections of (a) 15%mGO-ODA/MAPP; (b) 30%mGO-ODA/MAPP; (c) 45%mGO-ODA/MAPP; (d) 60%mGO-ODA/MAPP nylon composite films

Figures 1 and 2 show the SEM images of cross-sections of coated materials with different mGO-ODA contents and composite films, respectively. From Figure 1, it can be seen that the cross-sections of pure MAPP are very smooth, while the cross-sections of all composites are rough, which indicates that the mGO-ODA in the composites is well compatible with MAPP and the mechanical properties are improved.

And Figure 2 shows the good adhesion between the nylon film and the coating due to the hydrogen bonding and chemical bonding between the end groups of nylon and the anhydride part of MAPP.

Fig. (3) (a) Tensile stress-strain curves of different types of coatings, MAPP and nylon composite films; (b) elastic modulus diagram

393e39e971304b4db36051ea122547d

Figure 3 shows the tensile stress-strain curves (a) and elastic modulus diagrams (b) for different types of coatings, MAPP and nylon composite films.

The figure shows that the tensile strength and elastic modulus of the nylon composite film are greatly improved compared with the nylon film, and they increase with the increase of mGO-ODA content, which indicates that MAPP can improve the tensile strength and elastic modulus of the nylon film, and at the same time, graphene oxide also enhances the mechanical properties of the nylon composite film through the good interfacial bonding between MAPP and nylon.

Gas barrier experiments and electrochemical corrosion experiments proved that the H2 and O2 barrier properties and corrosion resistance of the nylon composite film were improved.


aktuelle Artikel

Wie wählt man das geeignete POE-gepfropfte Maleinsäureanhydrid zur Verbesserung der Zähigkeit von Nylon?

Coace® W1A-F wurde speziell als Schlagzähigkeitsmoderator für PA6, PA66 und Polyamidsysteme entwickelt, die eine Verstärkung und Füllung benötigen. Seine besonderen Eigenschaften machen es zur perfekten Wahl für Anwendungen, bei denen erhöhte Schlagzähigkeit und Zähigkeit besonders wichtig sind.

Mehr lesen →

Neuer Durchbruch bei der Modifizierung von PBT: revolutionäre Anwendung von POE-g-GMA als Zähigkeitsmittel

Die Verwendung von POE-g-GMA als Zähigkeitsvermittler bei der PBT-Modifikation behebt nicht nur die Sprödigkeit von PBT-Materialien, sondern bietet auch neue Entwicklungsmöglichkeiten für die Kunststoffindustrie.

Mehr lesen →

Ist es notwendig, bei der Zugabe von Füllstoffen zu PP/PE-Verbundmaterialien einen Kompatibilisator hinzuzufügen?

Wenn man die Verwendung von PP-g-MAH-Verträglichkeitsvermittlern untersuchen möchte, kann man sich mit einem professionellen Chemielieferanten in Verbindung setzen, um Muster und technische Unterstützung zu erhalten. Ein Gespräch mit COACE hilft bei der Anpassung von Mischungen an bestimmte Anwendungsanforderungen.

Mehr lesen →

HINTERLASSEN SIE UNS EINE NACHRICHT